PENGARUH WAKTU PROSES SANDBLASTING TERHADAP KEKERASAN DAN STRUKTUR MIKRO PADA ALUMINIUM PADUAN ZN, CR, MG, CU

AMALI, FAHMI (2019) PENGARUH WAKTU PROSES SANDBLASTING TERHADAP KEKERASAN DAN STRUKTUR MIKRO PADA ALUMINIUM PADUAN ZN, CR, MG, CU. Skripsi thesis, Institut Teknologi Dirgantara Adisutjipto.

	Text (ABSTRAK) 10040002_ABSTRAK.pdf Download (311kB)
	Text (BAB I) 10040002_BAB I.pdf Download (100kB)
	Text (DAFTAR PUSTAKA) 10040002_DAFTAR PUSTAKA.pdf Download (45kB)
	Text (FULL SKRIPSI) 10040002 - converted.pdf Restricted to Repository staff only Download (591kB)

Abstract

This study aims to determine the effect of sandblasting time on hardness and microstructure in aluminum alloy materials Zn, Cr, Mg, Cu. The Vickers hardness was calculated using the given load and the average diagonal length with the variations of 1 minute, 1.5 minutes, and 2 minutes. The total calculation of Vickers hardness was used to compare the value of material hardness without treatment with material that has been carried out by the sandblasting process. The results calculation of hardness material without treatment were 151.4 kgf/mm². The variation of 1 minute time was 220.5 kgf/mm² (50μm), 206 kgf/mm² (250μm), and 160.4 kgf/mm² (1000μm). The variation of 1.5 minutes was 228.3 kgf/mm² (50μm), 206 kgf/mm² (250μm), and 160.4 kgf/mm² (1000μm). And the 2 minute variation was 245.2 kgf/mm² (50μm), 213 kgf/mm² (250μm), and 165.2 kgf/mm² (1000μm). The results of microstructure testing indicated the differences in the density of the micro structures in each part.