ANALISIS KEKUATAN BENDING PADA KOMPOSIT SERAT KARBON DAN KOMPOSIT SERAT ARAMID MENGGUNAKAN RESIN EPOXY

Rinanda, Yendri (2023) ANALISIS KEKUATAN BENDING PADA KOMPOSIT SERAT KARBON DAN KOMPOSIT SERAT ARAMID MENGGUNAKAN RESIN EPOXY. Thesis thesis, Institut Teknologi Dirgantara Adisutjipto.

	Text (16050102) 16050102_ABSTRAK.pdf Download (183kB)
	Text (BAB I) 16050102_BAB 1.pdf Download (193kB)
	Text (DAFTAR PUSTAKA) 16050102_DAFTAR PUSTAKA.pdf Download (155kB)
	Text (FULL SKRIPSI) 16050102.pdf Restricted to Repository staff only Download (5MB)

Abstract

The aviation industry is very fast where in this industry requires components to build an airplane from various kinds of metal and non-metal materials. This study focuses on bending testing to determine the bending strength between Carbon fiber and Aramid fiber. The manufacture of Carbon fiber and Aramid Woven Roving fiber composites [0 °, 90°] uses the hand lay up method, referring to the ASTM (American Society for Testing Material) D790-02 standard. And use Epoxy resin. Results of the bending test for carbon fiber and aramid fiber were obtained at 60% volume fraction, the bending strength value was higher than the 70% volume fraction for both fiber types, namely 17.558 MPa for carbon fiber and 17.338 MPa for Aramid fiber. macro photo testing of carbon fiber and aramid fiber observed that aramid fiber is more ductile than carbon fiber.

Actions (login required)

View Item

Downloads